Abstract
Friction self-piercing riveting (FSPR) is a unique hybrid joining technique that combines the advantages of mechanical interlocking, frictional heat, and solid-state joining (if metallurgically compatible) to produce crack free joints in high strength and/or low-ductility alloys at room temperature. In the current study, Al-7055 sheets were joined using FSPR for lightweight automotive applications and significant microhardness variations were observed across the joint cross-section. A detailed microstructural characterization at multiple length scales was carried out using advanced electron microscopy and X-ray scattering techniques to provide a fundamental understanding of the process-structure-property relationships. The relative contributions of microstructural characteristics at various length scales (i.e., grain size, dislocation density, solute concentration, precipitate nature) to strengthening were estimated using existent formulations (i.e., Hall-Petch, Taylor, precipitate bypass/shear equations) and correlated to the observed microhardness values across different regions. Small-angle X-ray scattering and scanning transmission electron microscopy revealed significant changes in the size and volume fraction of precipitate species, i.e., GP-I Zones, η′, and Mg/Zn solute co-clusters, depending on the process region. It was observed that the dissolution of the small η′/GP-I zones (T ∼ 150–200 °C) in the heat-affected zone were the key reason for the hardness drop. Further, it was shown that solid-solution, dislocation, grain size and solute co-cluster strengthening played a key role in the thermo-mechanically affected zone and grain-refined zone (GRZ). Finally, these observations were leveraged along with the Zener-Holloman relationship and grain size in the GRZ to estimate the peak joining temperature of the GRZ (∼ 350 °C) near the steel rivet.