Phase Stability and Electrochemical Performance of La-Site-Doped Li6La3Zr0.5Nb0.5Ta0.5Hf0.5O12 High-Entropy Garnets

Abstract

We investigate La-site substitution in the high-entropy garnet Li6La3Zr0.5Nb0.5Ta0.5Hf0.5O12 (LLZNTH) using Ba2+, Sr2+, and Sm3+ to elucidate how dopant governs phase stability, Li-site distribution, and electrochemical behavior. X-ray diffraction shows that Sr2+ is incorporated homogeneously into the garnet lattice, whereas the larger Ba2+ and smaller Sm3+ ions partially exceed the structural tolerance, generating secondary phases. Nevertheless, the Sm-doped composition (x = 0.05) exhibits the highest room-temperature ionic conductivity (2.7 × 10–4 S cm–1). Neutron powder diffraction reveals that Sm substitution drives a redistribution of Li+ from the tetrahedral 24 d sites into the higher-mobility 96 h positions, enhancing the connectivity of the three-dimensional Li-ion migration network. A Sm-doping series (x = 0.01–0.05) further shows that only sufficiently high Sm levels induce this redistribution, whereas lower concentrations retain Li arrangements similar to the undoped garnet. Critical current density measurements demonstrate that La-site dopants also influence interfacial stability against Li metal, underscoring a trade-off between bulk transport enhancement and mechanical robustness. Collectively, these findings reveal that in high-entropy garnets improved ionic conductivity can originate not only from phase-pure structures but also from targeted modification of the Li sublattice, even when accompanied by secondary phases, offering a compositional design principle for garnet electrolytes.