An Organic Carboxylate Host for Stable Sodium Metal Batteries

Abstract

Sodium metal batteries (SMBs) hold great promise for the development of high-energy, sustainable energy storage solutions, but their practical deployment is hampered by unstable solid electrolyte interphases, uncontrollable sodium dendrite growth, and low Coulombic efficiency (CE) during repeated Na plating/stripping cycles. To address these challenges, we introduce an organic interlayer, containing perylenetetracarboxylic dianhydride sodium salt (Na4PT), on the surface of Cu current collector. This interlayer forms a sodiophilic organic interphase that lowers the nucleation barriers for sodium deposition and guides the formation of the interphase through polar carbonyl/carboxylate sites and a π-conjugated organic framework. A dendrite-free sodium metal anode is achieved using Na4PT coated Cu current collector. Under capacity-limited Na plating/stripping, Na||Na4PT@Cu half-cells deliver reversible capacities of 500 and 1,000 mAh g−1 at 0.1 and 1 A  g−1 for 500 cycles with average CE above 99%. Post-cycling scanning electron microscopy and X-ray photoelectron spectroscopy measurements confirm that Na4PT@Cu promotes compact and uniform Na deposits and supports the formation of a stable interphase with reduced parasitic decomposition, directly correlating interfacial chemistry/morphology with high plating/stripping reversibility. These results highlight organic carboxylate coating as a practical interface engineering strategy for dendrite-free SMBs.