Neutron Diffraction Residual Stress Characterization of Large-Scale Components by WA-DED

Abstract

Two large scale 316L stainless steel cylindrical shells were fabricated by wire arc directed energy deposition (WA DED). Residual stresses were measured by neutron diffraction, and the microstructure and mechanical properties of the printed material were characterized. Longitudinal and transverse residual stresses were compressive at the inner diameter, near neutral at mid wall, and tensile at the outer diameter; radial (through thickness) residual stresses were relatively low in magnitude, and peak tensile residual stresses occurred at the outer diameter surface along the longitudinal direction. The printed 316L SS exhibited a heterogeneous microstructure with finely dispersed δ ferrite, and demonstrated high yield and tensile strengths with large elongation and ductile fracture at ambient temperature and at 250 °C. These results indicate that the outer diameter surface and near surface regions—where tensile residual stress is highest—are the most vulnerable to residual stress–sensitive failure modes, such as stress corrosion cracking and fatigue.