Promising performance of sulfide catholytes compared to halide alternatives in NMC811 cathodes for sheet-type sulfide solid-state batteries

Abstract

Sulfide-based solid-state batteries (SSBs) show promise in achieving energy densities over 350 Wh/kg, yet challenges persist with their incorporation of high-voltage, nickel-rich layered oxide cathodes, such as LiNi₀. ₈Mn₀.₁Co₀.₁O₂ (NMC811), due to the poor oxidation stability of sulfide solid-state electrolytes (SSEs) like Li₆PS₅Cl (LPSCl). Although halide SSEs such as Li₃InCl₆ (LIC) and Li₃YCl₆ (LYC) have previously shown promise in stabilizing high-voltage NMC cathodes, our research reveals that sulfide SSE catholytes, particularly when combined with surface-coated NMC cathodes, deliver superior performance. This investigation assesses the cycling stability of various catholytes—LPSCl, LIC, Li₁₀GeP₂S₁₂ (LGPS), combined LIC-LPSCl, and LYC-LPSCl—in SSBs with LiNbO₃-coated NMC811 cathodes against sheet-type LPSCl separators. Findings indicate that while LGPS- based cathodes maintain higher capacity retention, they yield lower deliverable capacity, and LIC cathodes experience significant electrochemical degradation. Importantly, our results underscore that sulfide SSE catholytes, in conjunction with LiNbO₃-coated cathodes, optimize the cathode-electrolyte interphase (CEI), enhancing both kinetics and mass transport. These insights provide a strategic direction for optimizing catholyte composition in the development of sheet-type sulfide-based SSBs.