Abstract
Phase change materials (PCMs) that undergo a phase transition may be used to provide a nearly isothermal latent heat storage at the phase change temperature. This work reports the energy storage material cost ($/kWh) of various PCMs with phase change between 0-65°C. Four PCM classes are analyzed for their potential use in building systems: 1) inorganic salt hydrates, 2) organic fatty acids, 3) organic fatty alcohols, and 4) organic paraffin waxes. Many salt hydrates have low material costs (0.09 - 2.53 $-kg-1), high latent heat of fusion (100-290 J-g-1), and high densities (1.3-2.6 g-cm-3), leading to favorable volumetric storage density and low energy storage costs, 50-130 kWh-m3 and 0.90-40 $-kWh-1, respectively. Some salts are notably more expensive due to their scarcity or pressures from competing industries such as lithium-based salts. Fatty acids have the lowest energy storage cost in the temperature range 8-17°C at 6.50 – 40 $-kWh-1. Despite favorable latent heat (125 – 250 J-g-1) their low density gives (0.9 g-cm3) gives poor volumetric storage capacity, 32 – 80 kWh-m3. Fatty alcohols generally have high material costs 2.50 – 200 $-kg-1 which leads to high energy storage costs, 40-3000 $/kWh. With latent heat and density similar to fatty acids, fatty alcohols have poor volumetric energy storage, 43 – 55 kWh-m-3. Paraffin waxes containing only a single length carbon chain have a higher energy cost (15 – 500 $-kWh-1) than generic paraffin waxes containing many lengths of carbon chains (7 – 30 $-kWh-1). Pure waxes have a discrete phase change temperature due to their homogeneity. In contrast, a less refined generic wax with several carbon chain lengths is more likely to have a pronounced temperature glide during its phase change. Pure single carbon chain waxes are generally required for applications 5°C), incongruent melting, and corrosiveness. All PCMs may degrade if exposed to ambient conditions and therefore require proper sealing.