Single-crystal NMC622 from combustion-assisted solid-state synthesis: Tunable particle size, voltage-dependent stability, and Li-ion diffusion

Abstract

Cost-effective and scalable synthesis of single-crystal lithium–metal-oxide cathodes with controlled size and morphology remains challenging for advancing high-performance lithium-ion batteries. Here, we demonstrate a solution combustion–assisted solid-state method for producing single-crystal NMC622 with tunable particle size at various lithium stoichiometries. Structural and electronic characteristics were probed using synchrotron-XANES, EXAFS, XRD and XPS, confirming well-defined coordination environments and phase purity up to Li ≈ 1.3. The electrochemical behavior of LixNMC (x = 1.0 and 1.3) single crystals was evaluated across 2.8–4.3 V and 2.8–4.7 V windows to elucidate the effects of lithium content and operating voltage. At 2.8–4.3V, Li1.3NMC exhibits higher initial capacity due to its larger lithium inventory, while Li1.0NMC shows superior long-term retention driven by its larger crystal size and reduced structural distortion. Increasing the cutoff voltage to 4.7 V enhances the initial capacity of both compositions by 17–25%, but long-term capacity retention ultimately converges to values comparable to those at 4.3 V due to voltage-induced degradation, where Li+ diffusion constant remains lying ranging from 10−12 –10−11 cm2s−1. Overall, this study establishes a scalable combustion-assisted route for synthesizing tunable single-crystal NMC622 and highlights the interplay between lithium stoichiometry, particle size, and voltage window in governing cathode stability.