Effect of 316 stainless steel powder processing conditions on microstructure

Abstract

One parameter that has both economic and performance effects in the manufacturing of steel parts is the powder feedstock used. 316 L steel powder can be produced through water atomization or gas atomization, where both the powder size and the atomization process determine the cost of powder feedstock. Gas atomized powder is spherical and has a lower oxygen content than water atomized powder, making it the preferred choice for performance, but comes at a higher financial cost. In this study, various 316 L powder batches are characterized to understand physical properties and microstructural variations. Density and flowability were determined using gas pycnometry and Hall flow tests. Powder morphology and porosity were qualitatively analyzed via optical microscopy and scanning electron microscopy, Finally, transmission electron microscopy was used to determine changes in phases present. Spherical gas atomized powder of 30–100 μm contained Mnsingle bondSi rich oxides both on the surface and within the matrix. Meanwhile, irregular water atomized powder 30 μm in diameter contained silicon oxides without manganese. All powder particles contained a nickel rich cellular structure which was shown to support the formation of additional phases. While literature has observed general microstructural features across 316 L powder particles, transmission electron microscopy (TEM) in this study has identified variations in precipitation and cell structures. Information regarding morphology, flowability, density, and phase distributions can be applied to understand variations in part consolidation, which will in turn show which powder aspects are significant for production.