Controlled lithium stripping enables a stable interface for long-cycling anode-free solid-state batteries

Abstract

Anode-free solid-state batteries (AFSSBs) are a promising route toward achieving high energy density. In these cells, the anode contains no pre-stored lithium (Li). Instead, the entire Li inventory originates from the cathode and is freshly deposited onto a bare current collector during charging. However, achieving uniform and defect-free Li plating on this bare current collector remains a major challenge, often resulting in low Li plating/stripping efficiency and rapid capacity decay. Here, for the first time, operando neutron imaging is employed to visualize Li plating/stripping behavior in an anode-free full cell with LiNi0.82Mn0.07Co0.11O2 (NMC) as the cathode. Operando measurements reveal that complete stripping of Li leaves isolated Li residues on the current collector, which degrades the interfacial contact between the current collector and the solid-state electrolyte. To mitigate this interfacial issue and promote more uniform Li deposition, we implement a discharge-cutoff-voltage strategy that intentionally retains a thin residual Li layer after stripping. This preserved Li-containing interfacial reservoir not only improves interfacial contact but also serves as an in situ formed seed layer that enables more homogeneous subsequent Li plating. As a result, the optimized anode-free cell with limited stripping depth exhibits excellent long-term cycling stability, maintaining a discharge capacity of 112.1 mAh g−1 with a capacity retention of 80.6% and an average coulombic efficiency of approximately 99.9% after 500 cycles at 0.25 C. In contrast, the cell with a conventional discharge cutoff voltage of 2.8 V exhibits rapid capacity decay, retaining only 59.7 mAh g−1 after 50 cycles with a capacity retention of 40.7%. This work demonstrates that limiting deep stripping to preserve a thin Li-containing interfacial layer can effectively improve the cycling stability of sulfide-based AFSSBs.